Hyper PLA Plus Filament in Multiple Colors 10KG 1.75mm
$99.99
$189.99
500MM/S High-Speed Printing
The UJOYBIO Hyper PLA Filament is engineered for high-speed 3D printing, supporting speeds up to 500 mm/s. Its superior layer adhesion ensures that your prints are structurally stable and rich in detail, even at such high speeds.
Superior Strength & Toughness
This PLA+ filament boasts mechanical properties that are 60% higher than standard PLA+, with an impact strength increase of 130%. The result is a filament that offers exceptional durability and resilience, perfect for demanding 3D printing projects.
Neat Winding & Minimal Tangling
UJOYBIO utilizes a high-precision, fully automated wire winding process for its PLA Pro Filament. This ensures that the filament is neatly wound, minimizing tangles and knots during printing, which in turn saves you time and avoids frustration.
Consistent Diameter & Smooth Feeding
The UJOYBIO Hyper PLA Filament maintains a consistent 1.75mm diameter with an accuracy of ±0.02mm. This precise manufacturing process guarantees smooth feeding and reliable prints, ensuring that your 3D projects come out perfectly every time.
Environmentally Friendly & Premium Materials
Crafted from high-quality, plant-based starch materials, this filament is not only strong but also eco-friendly. It emits low levels of fumes during printing and is free from irritating odors. Additionally, the filament comes on fully recyclable cardboard spools, making it an excellent choice for environmentally conscious users.
Universally compatible with the majority of 1.75mm FDM 3D printers, ensuring seamless integration and reliable performance across popular models.
| Color | Red, Green,, Yellow, Gray, Orange, Blue, Pink, Brown, Olive Green. | ||
| Weight(1KG/set) | 1KG/roll(2.2lbs) | Diameter | 1.75 mm ± 0.02 mm |
| Tensile Strength(Z) | 31.1 MPA | Density | 1.32 G/CM³ |
| Tensile Modulus(Z) | 2630 MPA | Melt Flow Rate* | 4-7 G/10MIN |
| Elongation at Break | 2% | Heat Distortion Temperature | 55 °C |
| Flexural Strength(X-Y) | 70.7 MPA | Printing Temperature | 210~220 °C |
| Flexural Modulus(X-Y) | 2630 MPA | Bed Temperature | NO/40~60 °C |
| Charpy impact strength(X-Y) | 14 KJ/m² | Printing Speed | 300~500 MM/S |
| IZOD Impact Strength(X-Y) | 13 KJ/m² | Recommended Printing Temperature | 220 °C |
| *THE MELT FLOW RATE WAS TESTED AT 190°C, 2.16 KG. | |||